635-1063C High Temp Brazing Alloy Spheres

SCIENTIFIC ALLOY #
DEGREES CENTIGRADE
SCIENTIFIC ALLOY
DEGREES FAHRENHEIT
SPECIFIC GRAVITY gm/cm³
LIQUIDUS SOLIDUS LIQUIDUS SOLIDUS
SAC 2160
 635
625
50 Ag  18Cd 16.57 Zn 15.5 Cu 
1175
1160
9.185
SAC 2170
650
620
56 Ag.  22Cu. 17 Zn 5 Sn
1205
1145
9.21
SAC 1920
660
100 AL
1220
2.7
SAC 2180
690
630
50 AG, 16 CD, 15.5 CU, 15.5 ZN 3 NL
1270
1170
9.213
SAC 2190
700
605
35 AG. 26 CU 21 ZN 18 CD
1295
1125
8.88
SAC 2110
705
640
80 CU. 15 AG. 5 P
1300
1185
7.62
SAC 1790
705
630
61 AG 24 CU 15 IN 
1301
1166
9.483
SAC 2120
710
605
30 AG 27 CU 23 ZN 20 CD
1310
1125
8.765
SAC 2140
720
600
80 AG, 30 CU, 10 SN
1325
1115
9.58
SAC 1930
780
EUT 
780
72 AG, 28 CU 
1436
EUT 
1436
10.01
SAC 2200
785
775
71.5 AG  28 CU  5 NI
1445
1427
10.002
SAC 1940
800
370
98 AU 2 SI 
1472
698
16.92
SAC 2210
800
690
63 AG. 28.5 CU  6 SN 2.5 NI
1472
1275
9.714
SAC 1950
890
EUT
890
80 AU 20 CU
1634
EUT
1634
15.67
SAC 1960
950
EUT
950
82 AU  18 NI
1742
EUT
1742
15.92
SAC 2070
961
100 AG
1762
10.5
SAC 2080
985
665
85 CU,8 SN, 7 AG
1805
1225
8.87
SAC 1980 
1020
1000
50 AU 50 AG 
1868
1832
13.6
SAC 1990
1030
360
99.4 AU .8SB
1886
680
19.08
SAC 2220
1030
1025
99 AU 1 GA
1886
1877
18.872
SAC 2000
1063
100 AU
1945
19.3
SAC 2230
1063
99.8-99.9 AU. 0.1-0.2P
1945
18.34